现货PC/PBT 5220U 基础创新塑料 冲击改性 耐低温冲击
SABIC Innovative Plastics Xenoy? 5220U PBT+PCPolymer,Thermoplastic,Polycarbonate (PC),Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced,Polyester, TP,Polybutylene Terephthalate (PBT)SABIC Innovative Plastics (GE Plastics)产品说明:Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.
SABIC Innovative Plastics Xenoy? 5220U PBT+PC 物性表
比重 | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
密度 | 1.22 g/cc | 0.0441 lb/in3 | ISO 1183 |
水分吸收 | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
饱和吸水率 | 0.50 % | 0.50 % | ISO 62 |
线性成型收缩率,Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm | 0.0080 - 0.010 in/in @Thickness 0.126 in | SABIC Method |
线性成型收缩率,横向 | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on Tensile Bar; SABIC Method |
熔体流动速率 | 16 g/10 min @Load 5.00 kg, Temperature 250 °C | 16 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 |
化合物熔体指数 | 15 g/10 min @Load 5.00 kg, Temperature 250 °C | 15 g/10 min @Load 11.0 lb, Temperature 482 °F | MVR [cm^3/10 min]; ISO 1133 |
抗张强度(断裂) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 | |
抗张强度(屈服) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
伸长率 (断裂) | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
120 % | 120 % | 50 mm/min; ISO 527 | |
屈服伸长率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
拉伸模量 | 2.05 GPa | 297 ksi | 1 mm/min; ISO 527 |
2.25 GPa | 326 ksi | 50 mm/min; ASTM D638 | |
2.25 GPa | 326 ksi | 5 mm/min; ASTM D638 | |
弯曲强度 | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
弯曲模量 | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
悬壁梁缺口冲击强度 | 7.10 J/cm | 13.3 ft-lb/in | ASTM D256 |
2.99 J/cm @Temperature -40.0 °C | 5.60 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
5.30 J/cm @Temperature -30.0 °C | 9.93 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
50.0 kJ/m2 | 23.8 ft-lb/in2 | 80*10*4; ISO 180/1A | |
30.0 kJ/m2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
简支梁缺口冲击强度 | 5.50 J/cm2 | 26.2 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
落锤总能量 | 60.0 J @Temperature 23.0 °C | 44.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
耐电弧性 | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
热丝引燃 (HWI) | 15 - 30 sec | 15 - 30 sec | UL 746A |
高电弧燃烧,HAI | = 120 arcs | = 120 arcs | UL 746A |
高压电弧跟踪率,HVTR | 0.000 - 10.0 mm/min | 0.000 - 0.394 in/min | UL 746A |
线形热膨胀系数 - 流动 | 95.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 52.8 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
95.0 μm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
线性热膨胀系数,横向流动 | 90.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 50.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
90.0 μm/m-°C @Temperature -40.0 - 40.0 °C | ISO 11359-2 | ||
载荷下热变形温度(0.46 MPa) | 107 °C @Thickness 6.40 mm | 225 °F @Thickness 0.252 in | unannealed; ASTM D648 |
载荷下热变形温度(1.8 MPa) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
84.0 °C @Thickness 3.20 mm | 183 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
99.0 °C @Thickness 6.40 mm | 210 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
维卡软化温度 | 120 °C | 248 °F | Rate B/50; ISO 306 |
122 °C | 252 °F | Rate B/50; ASTM D1525 | |
125 °C | 257 °F | Rate B/120; ISO 306 | |
UL RTI | 75.0 °C | 167 °F | UL 746B |
UL RTI,机械冲击 | 75.0 °C | 167 °F | UL 746B |
UL RTI,机械无冲击 | 75.0 °C | 167 °F | UL 746B |
可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 |
Specific Volume | 0.83cm^3/g | ASTM D792 |
UV-light, water exposure/immersion | F2 | UL 746C |