| PC LV-2225Y 日本帝人化成公司 物性数据 |
| 规格级别： | --- | 外观颜色： | 冰色 |
| 用途概述： | --- | ||
| 备注说明： | 类型：易脱模型 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % |
| 物理性能 | 比重 | --- | JIS K-7112 | 1.20 | --- |
| 透光率 | 3mm thick | ASTM D-1003 | 88 | % | |
| 折射率 | --- | ASTM D-542 | 1585 | --- | |
| 阻燃性 | 0.38mm | UL 94 | V-2 | --- | |
| 机械性能 | 拉伸强度屈服点断裂点 | --- | ASTM D-638ASTM D-638 | 62(630)78(800) | Mpa(kgf/cm2)Mpa(kgf/cm2) |
| 拉伸模量 | --- | ASTM D-638 | 2130(21700) | Mpa(kgf/cm2) | |
| 拉伸率屈服点断裂点 | --- | ASTM D-638ASTM D-638 | 6140 | %% | |
| 弯曲强度 | --- | ASTM D-790 | 90(920) | Mpa(kgf/cm2) | |
| 弯曲模量 | --- | ASTM D-790 | 2260(23000) | Mpa(kgf/cm2) | |
| 压缩强度 | --- | ASTM D-695 | 76(780) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 830(85) | J/m(kgf・cm/cm) | |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 130(13) | J/m(kgf・cm/cm) | |
| 洛氏硬度 | --- | ASTM D-785 | 77 | M标度 | |
| 电气性能 | 耐导电径迹性（CTI） | --- | IEC 112 | 300 | V |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | kv/mm | |
| 体积电阻率 | --- | ASTM D-257 | 3×1016 | Ω.cm | |
| 介电率 | 60Hz | ASTM D-150 | 2.95 | --- | |
| 介电率 | 106Hz | ASTM D-150 | 2.9 | --- | |
| 介电正切 | 60Hz | ASTM D-150 | 0.0004 | --- | |
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | --- | |
| 耐电弧性 | --- | ASTM D-495 | 110 | ||