| 比重 | 1.58 | g/cm³ | No Standard |
| 熔流率 (320℃/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| 收缩率 (流动: 1.00 mm) | 0.10 | % | No Standard |
| (横向流动: 1.00 mm) | 0.60 | % | No Standard |
| 吸水率 (饱和, 40℃) | 1.0 | % | No Standard |
| 抗张强度 | 190 | MPa | ASTM D638 |
| 伸长率 (断裂) | 4.3 | % | ASTM D638 |
| 弯曲模量 | 10000 | MPa | ASTM D790 |
| 弯曲强度 | 240 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | 100 | J/m | ASTM D256 |
| 热变形温度 (1.8 MPa, 未退火) | 285 | ℃ | ASTM D648 |
| 玻璃转化温度 (DSC) | 125 | ℃ | No Standard |
| 熔融温度 | 306 | ℃ |
| 体积电阻率 | 1.0E+16 | ohm·cm | ASTM D257 |
| 介电强度 | 30 | kV/mm | ASTM D149 |
| 相对电容率 (10.0 GHz) | 3.40 | ASTM D150 | |
| 耗散因数 (10.0 GHz) | 0.010 | ASTM D150 | |
| 相比耐漏电起痕指数 (CTI) | PLC 1 | UL 746 |
| UL 阻燃等级 | V-0 | UL 94 |