| 比重 | 1.24 | g/cm³ | ASTM D792 |
| 熔流率 (190℃/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| 收缩率 (流动) | 0.30 到 0.50 | % | ASTM D955 |
| 抗张强度 (屈服) | 48.3 | MPa | ASTM D638 |
| 伸长率 (屈服) | 2.5 | % | ASTM D638 |
| 弯曲模量 | 3830 | MPa | ASTM D790 |
| 弯曲强度 | 82.7 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | 16 | J/m | ASTM D256 |