产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 8.0 | g/10min | |
| 密度 | ASTM D-1505 | 0.90 | g/cm3 | ||
| 机械性能 | 成型收缩率 | HPC Method | 1.6-1.8 | % | |
| 冲击强度 | ASTM D-256 | 3.5 | kg·cm/cm | ||
| 拉伸率 | ASTM D-638 | >500 | % | ||
| 洛氏硬度 | ASTM D-785 | 95 | R | ||
| 拉伸屈服强度 | ASTM D-638 | 290 | Kg/cm2 | ||
| 冲击强度 | ASTM D-256 | 8.0 | kg·cm/cm | ||
| 弹性挠曲模量 | ASTM D-790 | 16,000 | Kg/cm2 | ||
| 热性能 | 热变形温度 | ASTM D-648 | 120 | ℃ | |
| 耐热性 | 130℃老化 | HPC Method | >3,000 | hour | |
| 维卡软化点 | ASTM D-1525 | 145 | ℃ | ||