Test item 测试名称: Wood-based panels and surface decorated wood-based panels physicochemical properties test method 人造板及饰面人造板理化性能试验方法Test info 测试内容: Test itemTest standardLead timeSample size Others密度DensitySection 4.27 working days100×100mm, 5 pcs 含水率Moisture ContentSection 4.37 working days100×100mm, 5 pcs 极限体积膨胀率Limiting Volume SwellingSection 4.47 working days80×10×20mm(厚度不足20mm时,取实际厚度), 5 pcs 吸水厚度膨胀率Thickness Swelling after Water AbsorptionSection 4.57 working days50×50mm, 5 pcs需根据产品标准确定浸泡时间24小时吸水率24h Water AbsorptionSection 4.67 working days100×100mm, 5 pcs 极限吸水率Limiting Water AbsorptionSection 4.77 working days80×10×20mm(厚度不足20mm时,取实际厚度), 5 pcs 内结合强度Bonding Strength of Inner LayersSection 4.89 working days50×50mm, 15 pcs 静曲强度Flexural StrengthSection 4.97 working days长度:20h+50mm(h为样品公称厚度),但不得小于150mm宽度:50mm 10 pcs 弹性模量Flexural Modulus握螺钉力Screw Holding ForceSection 4.107 working days150×50mm, 5 pcs(做板面握钉力时,要求厚度不小于19mm,厚度不足时可多层胶合.做板边握钉力时,要求厚度不小于25mm,厚度不足时可3层胶合.需要胶合时样品数量适当增加.) 表面结合强度Bonding Strength of Surface LayerSection 4.139 working days50×50mm, 15 pcs 表面胶合强度Bonding Strength of Decorative LayerSection 4.149 working days50×50mm, 15 pcs 浸渍剥离性能Delamination after ImmersionSection 4.1775×75mm, 5 pcs需根据产品类别确定测试方法耐高温High Temperature ResistanceSection 4.187 working days30×20mm, 5 pcs 表面耐水蒸气性能Vapor Resistance of SurfaceSection 4.217 working days100×100mm, 5 pcs 顺纹抗压强度Compressive Strength parallel to Grain DirectionSection 4.2223×15×15mm, 10 pcs硬度HardnessSection 4.237 working days40×25mm, 5 pcs 表面吸收性能, Surface AbsorptionSection 4.247 working days300×100mm, 5 pcs湿循环性能Humidity CyclingSection 4.2525 working days湿循环测试后需做静曲强度、吸水厚度膨胀率和内结合强度测试. 样品尺寸具体参见相关测试项目.测试费用未包含静曲强度、吸水厚度膨胀率和内结合强度测试的费用水煮-冰冻-干燥处理后静曲强度Flexural Strength after Boiling-Freezing-Drying ConditioningSection 4.269 working days长度:20h+50mm(h为样品公称厚度),但不得小于150mm宽度:50mm 10 pcs 室外型人造板加速老化性能Accelerated Aging for Outdoor Use PanelSection 4.279 working days50×50mm, 15 pcs 表面耐龟裂性能Crazing Resistance of SurfaceSection 4.307 working days250×250mm, 5 pcs 表面耐冷热循环性能-方法1Resistance to Cold/Hot Cycling of Surface-Method 1 Sample for reference 参考图片:Sample Report 报告样本: