| 密度 | 885 | Kg/m³ | ASTM D1505 |
| 门尼料度 (ML1+4/100℃) | 5 | JIS K6395 | |
| MFR (190℃/2.16Kg) | 18 | g/10min | ASTM D1238 |
| (230℃/2.16Kg) | 34 | g/10min | ASTM D1238 |
| 断裂拉伸强度 | 12 | MPa | ASTM D638 |
| 断裂伸长率 | 950 | % | ASTM D638 |
| 扭曲刚性 | 9 | MPa | ASTM D1043 |
| 表面硬度 | 85 | Shore A | ASTM D2240 |
| 熔点 | 66 | ℃ | ASTM D2117 |
| 维卡软化点 | 56 | ℃ | ASTM D1525 |
| 脆化温度 | ＜-70 | ℃ | ASTM D746 |