| 熔体流动速率 | 25 | g/10min | ASTM D-1238 |
| 拉伸强度 | 370 | kg/cm | ASTM D-638 |
| 断裂伸长率 | 500 | % | ASTM D-638 |
| 弯曲模量 | 16000 | kg/cm | ASTM D-790 |
| 冲击强度 (23℃) | 2.5 | kg•cm/cm | ASTM D-256 |
| 洛氏硬度 | 100 | R | ASTM D-785 |
| 维卡软化点 | 150 | ℃ | ASTM D-1525 |
| 热变形温度 | 110 | ℃ | ASTM D-648 |
2023-12-19
220| 熔体流动速率 | 25 | g/10min | ASTM D-1238 |
| 拉伸强度 | 370 | kg/cm | ASTM D-638 |
| 断裂伸长率 | 500 | % | ASTM D-638 |
| 弯曲模量 | 16000 | kg/cm | ASTM D-790 |
| 冲击强度 (23℃) | 2.5 | kg•cm/cm | ASTM D-256 |
| 洛氏硬度 | 100 | R | ASTM D-785 |
| 维卡软化点 | 150 | ℃ | ASTM D-1525 |
| 热变形温度 | 110 | ℃ | ASTM D-648 |