规格用途
| 规格级别 | 外观颜色 | ||
| 该料用途 | |||
| 备注说明 | |||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.19 | g/cm3 | |
| 熔流率（熔体流动速率）(300°C/1.2kg) | ASTMD1238 | 10 | g/10min | ||
| 收缩率-流动(3.20mm) | InternalMethod | 0.60to0.80 | % | ||
| 机械性能 | 拉伸模量2 | ASTMD638 | 2270 | MPa | |
| 抗张强度3(屈服) | ASTMD638 | 62.0 | MPa | ||
| 抗张强度3(断裂) | ASTMD638 | 67.0 | MPa | ||
| 伸长率3(屈服) | ASTMD638 | 6.0 | % | ||
| 伸长率4(断裂) | ASTMD638 | 130 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 2370 | MPa | ||
| 弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 101 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 800 | J/m | |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 79.0 | J | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 137 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 126 | °C | ||
| 维卡软化温度 | ASTMD15255 | 143 | °C | ||
| 线形热膨胀系数-流动(-40到40°C) | ASTME831 | 6.8E-5 | cm/cm/°C | ||
| 线形热膨胀系数-横向(-40到40°C) | ASTME831 | 7.4E-5 | cm/cm/°C | ||
| RTIElec | UL746 | 130 | °C | ||
| RTIImp | UL746 | 120 | °C | ||
| RTIStr | UL746 | 130 | °C | ||
| 电气性能 | 耐电弧性6 | ASTMD495 | PLC7 | ||
| 相比耐漏电起痕指数(CTI) | UL746 | PLC2 | |||
| 高电弧燃烧指数(HAI) | UL746 | PLC3 | |||
| 高电压电弧起痕速率(HVTR) | UL746 | PLC3 | |||
| 热丝引燃(HWI) | UL746 | PLC2 | |||
| 可燃性 | UL阻燃等级 | 0.8mm | UL94 | V-2 | |
| 3.0mm | UL94 | V-0 | |||
| 灼热丝易燃指数(1.0mm) | IEC60695-2-12 | 960 | °C | ||
| 热灯丝点火温度(1.0mm) | IEC60695-2-13 | 850 | °C | ||
| 极限氧指数 | ISO4589-2 | 35 | % | ||