| 熔体流动速率 | 27 | g/10min | ASTM D-1238 |
| 密度 | 0.91 | g/cm | ASTM D-1505 |
| 洛氏硬度 | 80 | R标尺 | ASTM D-785 |
| 断裂伸长率 | 500 | % | ASTM D-638 |
| 屈服拉伸强度 | 250 | kg/cm | ASTM D-638 |
| 弹性模量 | 13000 | kg/cm | ASTM D-790 |
| IZOD冲击强度 | ASTM D-256 | ||
| (23℃) | 9 | kg.cm/cm | |
| (0℃) | 6 | kg.cm/cm | |
| (-20℃) | 5 | kg.cm/cm |
| 热变形温度 | 80 | ℃ |