| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 熔体流动速率 | 8 | g/10min | ASTM D-1238 |
| 收缩率 | MD|TD15|15 | 1/1000 |
| 降伏强度 | 270 | kg/cm | ASTM D-638 |
| 抗弯强度 | 13500 | kg/cm | ASTM D-790 |
| 硬度 | 91 | R | ASTM D-785 |
| IZOD缺口冲击强度 (-20℃) | 3.3 | kg.cm/cm | ASTM D-256 |
| 断裂伸长率 | 240 | % | ASTM D-638 |
| 断裂强度 | 210 | kg/cm | ASTM D-638 |
| IZOD冲击强度 (23℃) | 7.5 | kg.cm/cm | ASTM D-256 |
| 热变形温度 (4.6gf/cm) | 118 | ℃ | ASTM D-648 |
| 可燃性 | HB | UL 94 |