| 熔体流动速率 | 20 | g/10min | ASTM D-1238 |
| 洛氏硬度 | 110 | R | ASTM D-785 |
| 拉伸屈服强度 | 430 | kg/cm | ASTM D-638 |
| 断裂伸长率 | 50 | % | ASTM D-638 |
| 埃佐缺口冲击强度 (23℃) | 4 | kgcm/cm | ASTM D-256 |
| 弯曲模量 | 23000 | kg/cm | ASTM D-790 |
| 维卡软化点 | 156 | ℃ | ASTM D-1525 |
| 热变形温度 | 140 | ℃ | ASTM D-648 |