| 熔体流动速率 | 3.50 | g/10min | ASTM D-1238 |
| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 埃佐缺口冲击强度 (23℃) | 3 | kg.cm/cm | ASTM D-256 |
| 屈服点拉伸强度 | 350 | Kg/cm | ASTM D-638 |
| 肖氏硬度 | 100 | R scale | ASTM D-785 |
| 维卡软化点 | 152 | ℃ | ASTM D-1525 |
| 熔点 | 161 | ℃ | HPC |