| 熔体流动速率 | 28 | g/10min | ASTM D-1238 |
| 拉伸强度 | 210 | kg/cm | ASTM D-638 |
| 断裂拉伸强度 | 160 | kg/cm | ASTM D-638 |
| 断裂伸长率 | <300 | % | ASTM D-638 |
| IZOD缺口冲击强度 | ASTM D-256 | ||
| (-20℃) | 7 | kg.cm/cm | |
| (23℃) | >50(NB) | kg.cm/cm | |
| 弯曲模量 | 10000 | kg/cm | ASTM D-790 |
| 洛氏硬度 | 72 | R | ASTM D-785 |
| 热变形温度 | 110 | ℃ | ASTM D-648 |