所以外壳材料的选用非常重要；缓冲层在遇到大力冲击时起到缓冲效果，通常选用能吸收碰撞能量、无毒、无害、吸汗、透气的材料制成，大部分缓冲层采用发泡苯乙烯（EPS）材料。
PC 基础创新塑料(美国) 3413R-131 30%玻纤增强 注塑级
产品说明：
30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058". Internal mold release added.
| 比重 | ASTM D792 | ||
| -- | 1.43 | g/cm³ | ASTM D792 |
| -- | 1.44 | g/cm³ | ASTM D792 |
| 特定体积 | 0.697 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 300°C/1.2 kg | 5.0 | g/10 min | ASTM D1238 |
| 300°C/5.0 kg | 19 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.10 到 0.30 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.14 | % | ASTM D570 |
| 平衡, 23°C | 0.26 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 92 | ASTM D785 | |
| R 级 | 120 | ASTM D785 |
| 抗张强度 1(断裂) | 100 | MPa | ASTM D638 |
| 伸长率 2(断裂) | 2.0 | % | ASTM D638 |
| 弯曲模量 3(50.0 mm 跨距) | 6610 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 50.0 mm 跨距) | 153 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 24.0 | mg | ASTM D1044 |
| 悬壁梁缺口冲击强度 (23°C) | 110 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 1100 | J/m | ASTM D4812 |
| 落锤冲击 (23°C) | 5.00 | J | ASTM D3029 |
| 拉伸冲击强度 5 | 67.0 | kJ/m² | ASTM D1822 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 151 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 146 | °C | ASTM D648 |
| 维卡软化温度 | 165 | °C | ASTM D1525 6 |
| 线形热膨胀系数 - 流动 (-40 到 95°C) | 2.2E-5 | cm/cm/°C | ASTM E831 |
| 比热 | 1130 | J/kg/°C | ASTM C351 |
| 导热系数 | 0.22 | W/m/K | ASTM C177 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 体积电阻率 | > 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Air) | 19 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.35 | ASTM D150 | |
| 60 Hz | 3.35 | ASTM D150 | |
| 1 MHz | 3.31 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 1.1E-3 | ASTM D150 | |
| 60 Hz | 1.1E-3 | ASTM D150 | |
| 1 MHz | 7.0E-3 | ASTM D150 | |
| 耐电弧性 7 | PLC 7 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 5 | UL 746 | |
| 高电弧燃烧指数(HAI) | PLC 4 | UL 746 | |
| 高电压电弧起痕速率 (HVTR) | PLC 3 | UL 746 | |
| 热丝引燃 (HWI) | PLC 0 | UL 746 |
| UL 阻燃等级 | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.47 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，大 | 48 | hr | |
| 建议的大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 60 | % | |
| 料筒后部温度 | 293 到 316 | °C | |
| 料筒中部温度 | 304 到 327 | °C | |
| 料筒前部温度 | 316 到 338 | °C | |
| 射嘴温度 | 310 到 332 | °C | |
| 加工（熔体）温度 | 316 到 338 | °C | |
| 模具温度 | 82.2 到 116 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.025 到 0.076 | mm |
PC 基础创新塑料(美国) 3413R-131 30%玻纤增强 注塑级
供应
PC 基础创新塑料(美国) DMX9455 BK1066
PC 基础创新塑料(美国) EM
PC 基础创新塑料(美国) EXL9112R
PC 基础创新塑料(美国) EXL9330 BK1A233
PC 基础创新塑料(美国) HP2-1H111
PC 基础创新塑料(美国) LS2-6162
PC 基础创新塑料(美国) WR5210R GN1419
PC 基础创新塑料(美国)
PC 基础创新塑料(美国) 121R-701
PC 基础创新塑料(美国) 141R BK
PC 基础创新塑料(美国) 221R BK1B408
PC 基础创新塑料(美国) 4701R-701
PC 基础创新塑料(美国) 5832C
PC 基础创新塑料(美国) 920A-116
PC 基础创新塑料(美国) 945 WH4D146
PC 基础创新塑料(美国) 950A-116
PC 基础创新塑料(美国) BPL1000 BK
一般的自行车头盔是聚酯乙烯的，安全性更高一些的就用到碳纤维。其中，外壳是头盔的外层，在撞击时承受和分散冲击