TPU美国Lubrizol58300 耐水解性
Estane® 58300 TPUThermoplastic Polyurethane Elastomer (Polyether)
Lubrizol Advanced Materials, Inc.
产品说明：
Type: Polyether Thermoplastic Polyurethane (TPU)
Special Feature: Moisture Vapor Transmission, with Excellent Hydrolysis Resistance, Low Temperature and Wide Process Window
Processes: Extrusion: Blown, Flat Die Cast Film, Injection and Cable Jacketing
物性信息：
| 特性 | 可加工性，良好 耐水解性 |
| 用途 | Blown Film 电缆护套 电线电缆应用 流延薄膜 |
| 机构评级 | FDA 21 CFR 177.1680 FDA 21 CFR 177.2600 NSF 61 |
| RoHS 合规性 | RoHS 合规 |
| 外观 | 半透明 |
| 形式 | 粒子 |
| 加工方法 | 吹塑薄膜 电线&线缆挤出成型 挤出 注射成型 |
| 比重 | 1.10 | g/cm³ | ASTM D792 |
| 肖氏硬度 (邵氏 A) | 82 | ASTM D2240 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, H-18 转轮) | 22.0 | mg | ASTM D3389 |
| 水蒸气透过性 | 450 | g/m²/24 hr | ASTM E96 |
| Water Vapor Transmission - Mocon 1(38°C, 25.4 µm) | 1800 | g/m²/24 hr | ASTM D6701 |
| Kofler Melting Temperature | 125 | °C | 内部方法 |
| 拉伸变形 (200% 应变) | 11 | % | ASTM D412 |
| 拉伸应力 | ASTM D412 | ||
| 应变, 0.762 mm | 4.80 | MPa | ASTM D412 |
| 300%应变, 0.762 mm | 7.60 | MPa | ASTM D412 |
| 抗张强度 (断裂, 0.762 mm) | 37.9 | MPa | ASTM D412 |
| 伸长率 (断裂, 0.762 mm) | 650 | % | ASTM D412 |
| 撕裂强度 | |||
| 0.762 mm 2 | 69.6 | kN/m | ASTM D624 |
| 开裂 | 23 | kN/m | ASTM D470 |
| 玻璃转化温度 | -50.0 | °C | ASTM D3418 |
| 熔融温度 | 130 | °C | DSC |
| 干燥温度 | 104 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的大水分含量 | 0.020 | % | |
| 料筒1区温度 | 166 | °C | |
| 料筒2区温度 | 171 | °C | |
| 料筒3区温度 | 177 | °C | |
| 料筒4区温度 | 182 | °C | |
| 接头温度 | 182 | °C | |
| 熔体温度 | 179 | °C | |
| 口模温度 | 182 | °C |
| Screens: 20-40-80 meshDew Point: -40°C |
| 1 . | 90% RH |
| 2 . | C 模具 |
TPU美国Lubrizol58300 耐水解性