物理性能额定值单位测试方法
| 吸水率 (24hr,23℃) | 0.30 | % | ASTM D-570 |
| 熔体流动速率 (220℃/10.0kg) | 25 | g/10min | ISO 1133 |
| 比重 |
|
|
|
| 1.05 | g/cm | ASTM D-792 |
| 1.04 | g/cm | ISO 1183 |
| 模具收缩率 (流动) | 0.4-0.6 | % | ASTM D-955 |
机械性能额定值单位测试方法
| 拉伸模量 | 2700 | MPa | ISO 527-2/1 |
| 抗张屈服强度 |
|
|
|
| 49.0 | MPa | ASTM D-638 |
| 53.0 |
| ISO 527-2/50 |
| 断裂伸长率 |
|
|
|
| 35 | % | ASTM D-638 |
| >10 | % | ISO 527-2/50 |
| 弯曲模量 | 2450 | MPa | ASTM D-790 |
| 弯曲屈服强度 |
|
|
|
| 76.0 | MPa | ASTM D-790 |
| 81.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度 (23℃) | 17 | KJ/m2 | ISO 179/1eA |
| 悬壁梁缺口冲击强度 |
|
| ASTM D-256 |
| (-30℃,3.20mm) | 118 | J/m |
|
| (-30℃,12.7mm) | 80.0 | J/m |
|
| (0℃,3.20mm) | 157 | J/m |
|
| (℃,12.7mm) | 108 | J/m |
|
| (23℃,3.20mm) | 212 | J/m |
|
| (23℃,12.7mm) | 196 | J/m |
|
| 洛氏硬度 | 116 | R-scale | ASTM D-785 |
热性能额定值单位测试方法
| 热变形温度 |
|
|
|
| (1.80MPa.未退火.6.40mm) | 87.0 | ℃ | ASTM D-648 |
| (1.80MPa.未退火.12.7mm) | 92.0 | ℃ | ASTM D-648 |
| (1.80MPa.未退火) | 80.0 | ℃ | ISO 75-2/A |
| 阻燃等级 | HB |
| UL94 |
| 线形膨胀系数 (流动) | 0.000071 | cm/cm/℃ | ASTM D-696 |
| 导热系数 | 0.15 | W/m/K | ASTM C-177 |
电气性能额定值单位测试方法
| 表面电阻率 | >1.0E+16 | ohms | ASTM D-257 |
| 体积电阻率 (23℃) | >1.0E+16 | ohm.cm | ASTM D-257 |
| 介电强度 | 23 | KV/mm | ASTM D-149 |
| 介电常数 (1KHz) | 3.10 |
| ASTM D-150 |
| 耗散因数 (1KHz) | 0.0061 |
| ASTM D-150 |