| 密度 | 0.9 | g/cm | ASTM D-1505 |
| 熔体流动速率 (230℃,2.16kg) | 12.5 | g/10min | ASTM D-1238L |
| 断裂伸长率 | 12 | % | ASTM D-638 |
| 弯曲模量 | 16000 | kg/cm | ASTM D-790 |
| 洛氏硬度 | 104 | R scale | ASTM D-785 |
| IZOD冲击强度 (23℃) | 3 | kg.cm/cm | ASTM D-256 |
| 屈服拉伸强度 | 350 | kg/cm | ASTM D-638 |
| 热变形温度 (0.46N/mm) | 107 | ℃ | ASTM D-648 |