供应 沙特沙伯基础 LNP LUBRICOMP WFL36 compound PBT 润滑性介绍
LNP™ LUBRICOMP™ WFL36 compoundPolybutylene Terephthalate
SABIC Innovative Plastics
30% 玻璃纤维增强材料
产品说明：
LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound WFL-4036
Product reorder name: WFL36
物性信息：
| 黄卡编号 | E121562-101282605 |
| 填料/增强材料 | 玻璃纤维增强材料, 30% 填料按重量 |
| 添加剂 | PTFE润滑剂 (15%) |
| 特性 | 耐磨损性良好 润滑 |
| 加工方法 | 注射成型 |
| 比重 | 1.68 | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 | |||
| 流动 : 24小时 | 0.10 到 0.30 | % | ASTM D955 |
| 横向流动 : 24小时 | 0.50 到 1.0 | % | ASTM D955 |
| 垂直流动方向 : 24小时 | 0.50 到 1.0 | % | ISO 294-4 |
| 流动方向 : 24小时 | 0.10 到 0.30 | % | ISO 294-4 |
| 吸水率 | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.040 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| 抗张强度 (断裂) | 118 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 | |||
| 断裂 | 2.3 | % | ASTM D638 |
| 断裂 | 2.2 | % | ISO 527-2 |
| 弯曲模量 | |||
| -- | 10200 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| 弯曲强度 | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 187 | MPa | ISO 178 |
| 摩擦系数 | ASTM D3702 Modified | ||
| 与自身 - 动态 | 0.57 | ASTM D3702 Modified | |
| 与自身 - 静态 | 0.41 | ASTM D3702 Modified | |
| 磨损因数 - Washer | 42.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| 悬壁梁缺口冲击强度 | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 9.2 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23°C | 680 | J/m | ASTM D4812 |
| 23°C 3 | 43 | kJ/m² | ISO 180/1U |
| 装有测量仪表的落镖冲击 | |||
| 23°C, Energy at Peak Load | 13.7 | J | ASTM D3763 |
| -- | 2.61 | J | ISO 6603-2 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 218 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 4 | 214 | °C | ISO 75-2/Af |
| 线形热膨胀系数 | ASTM E831, ISO 11359-2 | ||
| 流动 : -40 到 40°C | 3.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 横向 : -40 到 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.050 | % | |
| 料筒后部温度 | 221 到 232 | °C | |
| 料筒中部温度 | 243 到 254 | °C | |
| 料筒前部温度 | 260 到 271 | °C | |
| 加工（熔体）温度 | 238 到 266 | °C | |
| 模具温度 | 82.2 到 98.9 | °C | |
| 背压 | 0.172 到 0.344 | MPa | |
| 螺杆转速 | 30 到 60 | rpm |