| 特性 | 尺寸稳定性良好 刚性，高 可加工性，良好 耐化学性良好 |
| 比重 | 1.31 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.00 mm) | 1.5 | % | ASTM D955 |
| 吸水率 (饱和) | 0.50 | % | ASTM D570 |
| 洛氏硬度 (R 级) | 112 | ASTM D785 |
| 抗张强度 1(3.20 mm) | 55.0 | MPa | ASTM D638 |
| 伸长率 2(断裂, 3.20 mm) | 100 | ASTM D638 | |
| 弯曲模量 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| 弯曲强度 4(3.20 mm) | 85.0 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (3.20 mm) | 40 | J/m | ASTM D256 |
| 落锤冲击 (3.20 mm) | > 84.0 | J | ASTM D3029 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 3.20 mm | 165 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 50.0 | °C | ASTM D648 |
| 维卡软化温度 | 200 | °C | ASTM D1525 5 |
| 线形热膨胀系数 - 流动 | 1.0E-5 | cm/cm/°C | ASTM D696 |
| 体积电阻率 | 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 | 140 | kV/mm | IEC 60243-1 |
| 漏电起痕指数 (解决方案 A) | 550 | V | IEC 60112 |
| UL 阻燃等级 (1.60 mm) | HB | UL 94 | |
| 热灯丝点火温度 (1.60 mm) | 550 | °C | AS/NZS 60695 |