耐磨PC DMX9455A--DMX9455A是一种标准流动、阻燃、透明的聚碳酸酯共聚物树脂，具有改进的耐刮性。

DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.

This data was supplied by SABIC-IP for the Americas region.

LEXAN™ PC DMX9455A>PC-FR<

聚合物: 共聚物

阻燃等级: HB • V-2 • V-0

熔融指数: 14.5 g/10min

缺口冲击: 3.06 kJ/m²

热变形温度: 133 °C

材料特性: 耐刮擦 • 中等流动性

PC DMX9455A物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

比重	1.20 g/cc	1.20 g/cc	ASTM D 792
密度	1.17 g/cc	0.0423 lb/in³	ASTM D 792
	1.17 g/cc	0.0423 lb/in³	ISO 1183
吸水率	0.080 % @Time 86400 sec	0.080 % @Time 24.0 hour	ASTM D 570
平衡吸湿	0.13 %	0.13 %	23°C / 50% RH; ISO 62
	0.13 %	0.13 %	50% RH; ASTM D 570
	0.28 % @Temperature 23.0 °C	0.28 % @Temperature 73.4 °F	ASTM D 570
	0.040 % @Time 86400 sec	0.040 % @Time 24.0 hour	50% RH; ASTM D 570
饱和吸水率	0.27 % @Temperature 23.0 °C	0.27 % @Temperature 73.4 °F	ISO 62
线性成型收缩率,Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	13 g/10 min @Load 1.20 kg, Temperature 300 °C	13 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
	14.5 g/10 min @Load 1.20 kg, Temperature 300 °C	14.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D 1238