沙特沙伯基础 LNP LUBRICOMP WFL34H compound PBT
LNP™ LUBRICOMP™ WFL34H compoundPolybutylene Terephthalate
SABIC Innovative Plastics
20% 玻璃纤维增强材料
产品说明：
LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare.
Also known as: LNP* LUBRICOMP* Compound WFL-4034 HC
Product reorder name: WFL34H
物性信息：
| 填料/增强材料 | 玻璃纤维增强材料, 20% 填料按重量 |
| 添加剂 | PTFE润滑剂 (15%) |
| 特性 | 耐磨损性良好 润滑 |
| 用途 | 医疗/护理用品 |
| 加工方法 | 注射成型 |
| 比重 | 1.59 | g/cm³ | ASTM D792 |
| 收缩率 | ASTM D955 | ||
| 流动 : 24小时 | 0.40 到 0.70 | % | ASTM D955 |
| 横向流动 : 24小时 | 0.90 到 2.0 | % | ASTM D955 |
| 吸水率 | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.070 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 8750 | MPa | ASTM D638 |
| -- | 8460 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 123 | MPa | ASTM D638 |
| 屈服 | 121 | MPa | ISO 527-2/5 |
| 断裂 | 123 | MPa | ASTM D638 |
| 断裂 | 121 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 3 | 2.8 | % | ASTM D638 |
| 屈服 | 2.7 | % | ISO 527-2/50 |
| 断裂 | 2.8 | % | ASTM D638 |
| 断裂 | 2.7 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| -- | 6840 | MPa | ASTM D790 |
| -- 4 | 7510 | MPa | ISO 178 |
| 弯曲强度 | |||
| -- | 176 | MPa | ASTM D790 |
| -- | 182 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 5 | 177 | MPa | ASTM D790 |
| 摩擦系数 | ASTM D3702 Modified | ||
| 与自身 - 动态 | 0.48 | ASTM D3702 Modified | |
| 与自身 - 静态 | 0.47 | ASTM D3702 Modified | |
| 磨损因数 - Washer | 35.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| 悬壁梁缺口冲击强度 | |||
| 23°C | 88 | J/m | ASTM D256 |
| 23°C 6 | 9.2 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23°C | 820 | J/m | ASTM D4812 |
| 23°C 7 | 46 | kJ/m² | ISO 180/1U |
| 装有测量仪表的落镖冲击 | |||
| 23°C, Total Energy | 9.60 | J | ASTM D3763 |
| -- | 3.20 | J | ISO 6603-2 |
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火, 3.20 mm | 223 | °C | ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距 8 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm | 213 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 9 | 209 | °C | ISO 75-2/Af |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.050 | % | |
| 料筒后部温度 | 221 到 232 | °C | |
| 料筒中部温度 | 243 到 254 | °C | |
| 料筒前部温度 | 260 到 271 | °C | |
| 加工（熔体）温度 | 238 到 266 | °C | |
| 模具温度 | 82.2 到 98.9 | °C | |
| 背压 | 0.172 到 0.344 | MPa | |
| 螺杆转速 | 30 到 60 | rpm |
| 1 . | 50 mm/min |
| 2 . | 类型 1, 5.0 mm/min |
| 3 . | 类型 1, 5.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*3 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |