SABIC Innovative Plastics NORYL GTX GTX820 PPE+PS+PA 物性表
| 比重 | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| 密度 | 1.245 g/cc | 0.04498 lb/in³ | ASTM D792 |
| 吸水率 | 0.50 % @Time 86400 sec | 0.50 % @Time 24.0 hour | ASTM D570 |
| 水分吸收 | 1.00 % | 1.00 % | 50% RH, 24 hrs; ASTM D570 |
| 线性成型收缩率,Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm | 0.0065 - 0.0085 in/in @Thickness 0.126 in | SABIC Method |
| 洛氏硬度（R 级） | 119 | 119 | ASTM D785 |
| 弯曲强度 | 194 MPa | 28100 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 5.96 GPa | 864 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.530 J/cm @Temperature -30.0 °C | 0.993 ft-lb/in @Temperature -22.0 °F | ASTM D256 |
| 线形热膨胀系数 - 流动 | 30.6 - 39.6 µm/m-°C @Temperature -20.0 - 150 °C | 17.0 - 22.0 µin/in-°F @Temperature -4.00 - 302 °F | ASTM E 831 |
| 载荷下热变形温度(0.46 MPa) | 254 °C |