4210G3 物性表
| 成型收缩率 | 0.4-1.0 | % | |
| 比重 | 1.45 | ASTM D792 |
| 抗拉降伏强度 | 895 | kg/cm | ASTM D638 |
| 弯曲弹性模数 | 55000 | kg/cm | ASTM D790 |
| 缺口冲击强度 | 4.8 | Kg.cm/cm | ASTM D256 |
| 绝缘破坏强度 | 23 | KV/mm | ASTM D149 |
| 抗电弧性 | 125 | sec | ASTM D495 |
| 热变形温度 |
2023-12-14
1104210G3 物性表
| 成型收缩率 | 0.4-1.0 | % | |
| 比重 | 1.45 | ASTM D792 |
| 抗拉降伏强度 | 895 | kg/cm | ASTM D638 |
| 弯曲弹性模数 | 55000 | kg/cm | ASTM D790 |
| 缺口冲击强度 | 4.8 | Kg.cm/cm | ASTM D256 |
| 绝缘破坏强度 | 23 | KV/mm | ASTM D149 |
| 抗电弧性 | 125 | sec | ASTM D495 |
| 热变形温度 |