德国巴斯夫UltramidPA6 B3G8高刚性玻纤40%尼龙6
| 收缩率 | 23℃ | % | 0,20到1,0 | |
| 拉伸应力 | 断裂,23℃ | MPa | 95.17到284.83 | |
| 拉伸应变 | 断裂,23℃ | % | 2,5到3,0 | |
| 拉伸模量 | 23℃ | MPa | 0.01,0.01E0.05到0.01,0.04E0.05 | |
| 热变形温度 | 1.8MPa,未退火 | °C | 239到261 | |
| 简支梁无缺口冲击强度 | 23℃ | kJ/m² | 10.679到17.642 | |
| 23℃ | kJ/m² | 0.882到3.762 |
2023-12-14
140德国巴斯夫UltramidPA6 B3G8高刚性玻纤40%尼龙6
| 收缩率 | 23℃ | % | 0,20到1,0 | |
| 拉伸应力 | 断裂,23℃ | MPa | 95.17到284.83 | |
| 拉伸应变 | 断裂,23℃ | % | 2,5到3,0 | |
| 拉伸模量 | 23℃ | MPa | 0.01,0.01E0.05到0.01,0.04E0.05 | |
| 热变形温度 | 1.8MPa,未退火 | °C | 239到261 | |
| 简支梁无缺口冲击强度 | 23℃ | kJ/m² | 10.679到17.642 | |
| 23℃ | kJ/m² | 0.882到3.762 |