Styrolution Terlux® 2802 TR MABS 物性表
| 吸水率 | 0.70 % | 0.70 % | ISO 62 |
| 平衡吸湿 | 0.35 % | 0.35 % | 23°C/50% R.H.; ISO 62 |
| 线性成型收缩率 | 0.0055 cm/cm | 0.0055 in/in | ASTM Data; MD |
| 熔体流动速率 | 2.0 g/10 min @Temperature 200 °C | 2.0 g/10 min @Temperature 392 °F | ISO 1133 |
| 抗张强度(屈服) | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | 2 in/min; ASTM Test | |
| 伸长率 (断裂) | 12 % | 12 % | 50mm/min, Nominal strain; ISO 527 |
| 屈服伸长率 | 4.0 % | 4.0 % | 50mm/min; ISO 527 |
| 拉伸模量 | 2.00 GPa | 290 ksi | 1mm/min; ISO 527 |
| 2.00 GPa | 290 ksi | ASTM Test | |
| 悬壁梁缺口冲击强度 | 0.690 J/cm @Thickness 3.17 mm | 1.29 ft-lb/in @Thickness 0.125 in | ASTM Test |
| 简支梁无缺口冲击强度 | 12.0 J/cm² | 57.1 ft-lb/in² | ISO 179 |
| 8.00 J/cm² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |
| 简支梁缺口冲击强度 | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| 0.200 J/cm² @Temperature -30.0 °C | 0.952 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 体积电阻率 | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| 介电常数 | 2.8 @Frequency 1.00e+6 Hz | 2.8 @Frequency 1.00e+6 Hz | IEC 60250 |
| 2.9 @Frequency 100 Hz | 2.9 @Frequency 100 Hz | IEC 60250 | |
| 耗散因数 | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 |
| 0.016 @Frequency 100 Hz | 0.016 @Frequency 100 Hz | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V | IEC 60112 |
| 线形热膨胀系数 - 流动 | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| 载荷下热变形温度(0.46 MPa) | 94.0 °C | 201 °F | annealed; ASTM Test |
| 94.0 °C | 201 °F | ISO 75 | |
| 载荷下热变形温度(1.8 MPa) | 90.0 °C | 194 °F | annealed; ASTM Test |
| 90.0 °C | 194 °F | ISO 75 | |
| 维卡软化温度 | 91.0 °C | 196 °F | Rate "A" Loading 1 (50 degC/h 10N); ASTM Test |
| 93.0 °C | 199 °F | (50 °C/h / 50N) - B/50; ISO 306 | |
| 玻璃化转变温度，Tg | 107 °C | 225 °F | 10 K/min; ISO 11357-1/-3 |
| Transmission, Visible | 80 % | 80 % | unknown thickness |
| 加工（熔体）温度 | 229 - 260 °C | 444 - 500 °F | Injection Molding |
| 250 °C | 482 °F | Injection molding | |
| 模具温度 | 48.9 - 73.9 °C | 120 - 165 °F | Injection Molding |
| 90.0 °C | 194 °F | Ejection temperature | |
| 射速 | 60.0 mm/sec | 2.36 in/sec | Injection molding |
| 干燥温度 | 70.0 °C | 158 °F | Injection Molding |
| 干燥时间 | 2 - 4 hour | 2 - 4 hour | Injection Molding |
| 水分含量 | 0.70 % | 0.70 % | ASTM Data |