Elastollan® S98ANThermoplastic Polyurethane Elastomer (Polyester)
BASF Corp. Thermoplastic Polyurethanes
产品说明：
Elastollan® S98AN is specifically formulated for injection molding applications with short cycling time. It exhibits good hydrolytic stability, excellent abrasion resistance, toughness, good heat, oil, fuel, and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® S98AN is supplied uncolored in diced form.
物性信息：
| 特性 | 抗溶剂性 良好的撕裂强度 良好耐磨损性 耐热性，高 韧性良好 水解稳定 |
| 外观 | 无色 |
| 加工方法 | 挤出 注射成型 |
| 比重 | 1.24 | g/cm³ | ASTM D792 |
| 肖氏硬度 (邵氏 D) | 55 | ASTM D2240 |
| 拉伸模量 (注塑) | 131 | MPa | ASTM D412 |
| 弯曲模量 (注塑) | 138 | MPa | ASTM D790 |
| 泰伯耐磨性 | 50.0 | mg | ASTM D1044 |
| Abrasion - DIN | 35 | mm³ | DIN 53516 |
| Softening Point - DMA | 133 | °C | 内部方法 |
| 拉伸应力 | ASTM D412 | ||
| 应变 | 21.4 | MPa | ASTM D412 |
| 应变 | 40.7 | MPa | ASTM D412 |
| 抗张强度 | 46.9 | MPa | ASTM D412 |
| 伸长率 (断裂) | 420 | % | ASTM D412 |
| 撕裂强度 1 | 210 | kN/m | ASTM D624 |
| 压缩变形 | ASTM D395B | ||
| 23°C, 22 hr | 30 | % | ASTM D395B |
| 70°C, 22 hr | 45 | % | ASTM D395B |
| 玻璃转化温度 | -14.0 | °C | 内部方法 |
| 维卡软化温度 | 157 | °C | ASTM D1525 |
| 干燥温度 | 110 到 120 | °C | |
| 干燥时间 | 2.0 到 3.0 | hr | |
| 建议的大水分含量 | 0.030 | % | |
| 料筒后部温度 | 210 到 230 | °C | |
| 料筒中部温度 | 210 到 230 | °C | |
| 料筒前部温度 | 210 到 230 | °C | |
| 射嘴温度 | 220 到 240 | °C |
| 1 . | C 模具 |
Copyright © souwuxing.com All Rights Reserved. 归 搜聚信息科技公司 所有
此数据由 搜聚 从该材料的生产商处获得。搜聚 大努力确保此数据的准确性,但是搜聚对这些数据值不承担任何责任，并强烈建议在*终选料前，就数据值与材料供应商进行验证。
附加功能
PDF物性文档下载
[普通版][去水印版]
替代物查询
加入对比
加入收藏
收起
请添加要对比的物