Ethylene Vinyl Acetate Copolymer
Hanwha Chemical
产品说明：
HANWHA EVA 2315 is manufactured by Dow tubular high pressure process and designed for variety of foam molding application such as shoes and sandals etc.. EVA 2315 is well known for its excellent processability and high assurance.
Excellent Foam Molding Property
Very Good Mechanical Properties
Excellent Loading Property of Various Fillers
物性信息：
| 特性 | 共聚物 可发泡性能 可加工性，良好 |
| 用途 | 泡沫 鞋类 |
| 形式 | 粒子 |
| 密度 | 0.950 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| 醋酸乙烯含量 | 15.0 | wt% | 内部方法 |
| 肖氏硬度 | ASTM D2240 | ||
| 邵氏 A | 93 | ASTM D2240 | |
| 邵氏 D | 40 | ASTM D2240 |
| 抗张强度 (断裂) | 14.7 | MPa | ASTM D638 |
| 伸长率 (断裂) | 820 | % | ASTM D638 |
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 维卡软化温度 | 66.0 | °C | ASTM D1525 |
| 熔融温度 | 88.0 | °C | ASTM D3417 |
| Processing Temperature | |||
| Kneader | 90 到 110 | °C | |
| Roll Mill | 100 | °C |
韩国韩华 EVA产品介绍
乙烯-醋酸乙烯共聚物，简称EVA。一般醋酸乙烯（VA）的含量在5%-40%，与聚乙烯（PE)相比，EVA由于在分子链中引入醋酸乙烯单体，从而降低了高结晶度，提高了韧性、抗冲击性、填料相溶性和热密封性能，被广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。
EVA特性
EVA是广泛用于发泡鞋材、功能性棚膜、包装模、热熔胶、电线电缆及玩具等领域。1、乙酸乙烯含量在5%以下的EVA，其主要产品是薄膜、电线电缆、LDPE改性剂、胶粘剂等；2、乙酸乙烯含量在5%~10% 的EVA产品为弹性薄膜等；3、乙酸乙烯含量在20~28%的EVA，主要用于热熔粘合剂和涂层制品。
EVA应用
(1)发泡鞋材。鞋材是我国EVA树脂主要的应用领域。在鞋材使用的EVA树脂中，醋酸乙烯含量一般在15%～22%。由于EVA树脂共混发泡制品具有柔软、弹性好、耐化学腐蚀等性能，因此被广泛应用于中旅游鞋、登山鞋、拖鞋、凉鞋的鞋底和内饰材料中。另外，这种材料还用于隔音板、体操垫和密封材领域。(2)薄膜。EVA薄膜的主要用途是生产功能性棚膜。功能性棚膜具有较高的耐候、防雾滴和保温性能，由于聚乙烯不具有极性，即使添加一定量的防雾滴剂，其防雾滴性能也只能维持2个月左右；而添加一定量EVA树脂制成的棚膜，不仅具有较高的透光率，而且防雾滴性能也有较大提高，一般可超过4个月。另外，EVA还可用于生产包装膜、医用膜、层压膜、铸造膜等。(3)电线电缆。随着计算机及网络工程的不断发展，出于对机房安全的考虑，人们越来越多地使用无卤阻燃电缆和硅烷交联电缆。由于EVA树脂具有良好的填料包容性和可交联性，因此在无卤阻燃电缆、半导体屏蔽电缆和二步法硅烷交联电缆中使用较多。另外，EVA树脂还被应用于制作一些特殊电缆的护套。在电线电缆中使用的EVA 树脂，醋酸乙烯含量一般在12%～24%。(4)玩具。EVA树脂在玩具中也有较多应用，如童车轮、座垫等。(5)热熔胶。以EVA树脂为主要成分的热熔胶，由于不含溶剂，不污染环境且安全性较高，非常适合于自动化的流水线生产，因此被广泛应用于书籍无线装订、家具封边、汽车和家用电器的装配、制鞋、地毯涂层和金属的防腐涂层上。(6)其他。EVA树脂在油墨、箱包、酒瓶垫盖等领域也有较为广泛的应用，估计这些方面消耗EVA树脂不少于15kt。