超高韧性 PA6 德国巴斯夫 BU50I 耐低温冲击 可焊接 安全帽 体育用品
Polyamide 6
BASF Corporation
产品说明：
Ultramid Ultratough Nylon BU50I is an unreinforced PA6, impact modified injection molding product that maintains its impact strength and ductility to -40 deg F (-40 deg C). The extreme low temperature tolerance of Ultratough Nylon BU50I makes it ideal for applications in which the weldline impact strength at low temperatures is critical.
Applications
Ultramid BU50I is generally recommended for automotive components, small engines, power tool parts and casings, cold weather and high impact supports gear, such as snowboards, ski components, helmets and hockey masks.
物性信息：
| 黄卡编号 | E |
| 添加剂 | 冲击改性剂 |
| 特性 | 超高韧性 冲击改性 可焊接 耐低温 耐低温冲击 耐油性能 延展性 |
| 用途 | 安全帽 动力/其它工具 汽车领域的应用 体育用品 |
| 机构评级 | EC 1907/2006 (REACH) |
| RoHS 合规性 | RoHS 合规 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 比重 | 1.06 | -- | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 1.8 | -- | % | |
| 吸水率 | ||||
| 饱和 | 7.3 | -- | % | ASTM D570 |
| 饱和, 23°C | 7.3 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.1 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| 拉伸模量 (23°C) | 1600 | 510 | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 屈服, 23°C | 50.0 | -- | MPa | ASTM D638 |
| 屈服, 23°C | 45.0 | 27.0 | MPa | ISO 527-2 |
| 断裂, 23°C | 45.0 | -- | MPa | ASTM D638 |
| 伸长率 | ||||
| 屈服, 23°C | 5.0 | -- | % | ASTM D638 |
| 屈服, 23°C | 4.0 | 42 | % | ISO 527-2 |
| 断裂, 23°C | > 100 | -- | % | ASTM D638 |
| 标称拉伸断裂应变 (23°C) | 40 | > 50 | % | ISO 527-2 |
| 弯曲模量 | ||||
| 23°C | 1690 | -- | MPa | ASTM D790 |
| 23°C | 1550 | 460 | MPa | ISO 178 |
| 弯曲强度 | ||||
| 23°C | 65.0 | -- | MPa | ASTM D790 |
| 23°C | 50.0 | 15.0 | MPa | ISO 178 |
| 简支梁缺口冲击强度 (23°C) | 95 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度 (23°C) | 无断裂 | -- | ISO 179 | |
| 悬壁梁缺口冲击强度 | ASTM D256 | |||
| -40°C | 无断裂 | -- | ASTM D256 | |
| 23°C | 无断裂 | -- | ASTM D256 | |
| 落下冲击阻力 (23°C) | 8.67 | -- | J/cm | 内部方法 |
| 载荷下热变形温度 (1.8 MPa, 未退火) | 50.0 | -- | °C | ASTM D648, ISO 75-2/A |
| 熔融峰值温度 | 220 | -- | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.800 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.800 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.800 mm | 65.0 | -- | °C | UL 746 |
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 74 |