Polyamide 6
Shakespeare Monofilaments and Specialty Polymers
产品说明：
Isocor™ 4007 is a high viscosity PA-6. This resin is specifically suited for applications re excellent abrasion, tensile and elongation properties. This resin can be processed using conventionalues.
Typical applications for Isocor™ 4007 include:
profile extrusions
film extrusions
flexible tubing
fiber and filaments
物性信息：
| 特性 | 良好的柔韧性 良好耐磨损性 粘度，高 |
| 用途 | 薄膜 管件 细丝 纤维 型材 |
| 形式 | 粒子 |
| 加工方法 | 薄膜挤出 型材挤出成型 注射成型 |
| 比重 | 1.10 | -- | g/cm³ | ASTM D792 |
| 收缩率 - 流动 (3.18 mm) | 1.5 | -- | % | ASTM D955 |
| 吸水率 (24 hr) | -- | 0.53 | % | ASTM D570 |
| 拉伸模量 | 1870 | 1640 | MPa | ASTM D638 |
| 抗张强度 | 52.6 | 53.8 | MPa | ASTM D638 |
| 悬壁梁缺口冲击强度 | 140 | 140 | J/m | ASTM D256 |
| 落锤冲击 | 36.2 | 36.2 | J | ASTM D3029 |
| 玻璃转化温度 | 120 | -- | °C | DSC |
| 熔融温度 | 213 | -- | °C | DSC |
| 干燥 Color, ASTM D1003-97: 9.68 LColor, ASTM D1003-97: -4.64 aColor, ASTM D1003-97: -6.68 b |
| Dew Point | < -17.8 | °C | |
| 建议的最大水分含量 | 0.20 | % | |
| 料斗温度 | 79.4 | °C | |
| 料筒后部温度 | 221 到 243 | °C | |
| 料筒中部温度 | 227 到 260 | °C | |
| 料筒前部温度 | 238 到 271 | °C | |
| 射嘴温度 | 238 到 271 | °C | |
| 加工（熔体）温度 | 238 到 271 | °C | |
| 模具温度 | 10.0 到 93.3 | °C | |
| 注塑压力 | 3.45 到 13.8 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | 0.689 | MPa |
| 建议的最大水分含量 | 0.10 | % | |
| 料筒温度 | 79.4 | °C | |
| 料筒1区温度 | 254 | °C | |
| 料筒2区温度 | 266 | °C | |
| 料筒3区温度 | 271 | °C | |
| 料筒4区温度 | 271 | °C | |
| 口模温度 | 260 | °C |
| Flange: 510°F (266°C)Air Dew Point (max): 0°F (-18°C)Neck: 510°F (266°C)Head: 500°F (260°C)Pump: 500°F (260°C)L/D Ratio: 24 to 30:1Compression Ratio: 3.5:1Polymer @ Die: 450°F (232°C)Screw Pressure: 2000 psi |