物性纠错
熔体质量流动速率 | 230°C/2.16kg | ASTMD1238 | 23 | g/10min |
拉伸强度2 | Break,2.00mm | ASTMD638 | 28.4 | Mpa |
伸长率2 | 断裂,2.00mm | ASTMD638 | 600 | % |
弯曲模量3 | 6.40mm | ASTMD790 | 137 | Mpa |
熔融峰值温度 | ASTMD3418 | 215 | °C | |
相比耐漏电起痕指数 | CTI)4 | UL746 | 600 | V |
漏电起痕指数 | 解决方案A | IEC60112 | 600 | V |
-40°C,6.40mm | ASTMD256 | NoBreak | ||
23°C,6.40mm | ASTMD256 | NoBreak | ||
肖氏硬度 | 邵氏D | ASTMD2240 | 44 |