| 拉伸强度 | Yield | MPa | ASTM D638 | 27.5 |
| 弯曲模量 | MPa | ASTM D790 | 539 | |
| 拉伸伸长率 | Break | % | ASTM D412 | 420 |
| 断裂强度 | kN/m | ASTM D624 | 186 | |
| 熔融指数 | 200℃/2.16kg | g/10min | ASTM D1238 | 27 |
| 密度 | g/cm³ | ASTM D792 | ||
| 吸水率 | 24hr，23℃ | % | ASTM D570 | 0.3 |
| 收缩率 | % | ASTM D955 | 1.7 |