代理PA66日本旭化成 1402G 玻璃纤维 加纤30%增强 抗热老化性 注塑级 汽车领域
2023-11-10
280
|
|
|
|
|
| 密度 | 干 | ASTM D-792 | 1.14 |
|
| ASTMD792 | 1.14 | g/cm³ |
| 收缩率 | MD2.0mm | ASTMD995 | 1.3 | % |
| TD2.0mm | ASTMD995 | 2.0 | % |
| 干 | 旭化成方法 | 1.3-2.0 | % |
| 吸水率 | (23°C,24hr) | ASTMD570 | 2.5 | % |
|
|
|
|
|
| 断裂伸长率 | 23°C | ASTMD638 | 50 | % |
| ASTM D638/ISO 527 | 50 | % |
| 断裂延伸率 | 干(湿) | ASTM D-638 | 50(250) | % |
| 抗挠强度 | 干(湿) | ASTM D-790 | 118(54) | Mpa |
| 抗挠系数 | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
| 拉伸强度 | 干(湿) | ASTM D-638 | 79(57) | Mpa |
| 23°C | ASTMD638 | 79 | Mpa |
| 洛氏硬度 | 干(湿) | ASTM D-785 | 120(108) | R scale |
| 干(湿) | ASTM D-785 | 80(55) | M Scale |
| 磨耗率 | 湿 | ASTM D-1044 | 7 |
|
| 弯曲模量 | 23°C | ASTMD790 | 2800 | Mpa |
| ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in |
| 弯曲强度 |
| ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in |
| 23°C | ASTMD790 | 118 | Mpa |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 39 | J/m |
| 悬臂梁式缺口冲击强度 | 干(湿) | ASTM D-256 | 39(147) | J/m |
| Charpy冲击强度 |
| ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
|
|
|
|
|
| 比热容 | 干 |
| 1670 | J/(kg.k) |
| 导热率 | 干 |
| 0.2 | W/(m.K) |
| 燃烧性（率） |
| UL94 | v-2 |
|
| 热变形温度 |
| ASTM D648/ISO 75 | 230 | ℃（℉） |
| 0.46MPa,干 | ASTM D-648 | 230 | ℃ |
| 1.82MPa,干 | ASTM D-648 | 70 | ℃ |
| 0.45MPa未退火 | ASTMD648 | 230 | °C |
| 1.80MPa未退火 | ASTMD648 | 70 | °C |
| 线膨胀系数 | 导热系数 | JISR2618 | 0.2 | W/m/K |
| 比热 |
| 1670 | J/kg/°C |
| 线性膨胀系数 | 干 | ASTM D-696 | 8 |
|
| ASTM D696/ISO 11359 | 8 | mm/mm.℃ |
| 阻燃性 | 干 | UL 94 | V-2 |
|
|
|
|
|
|
| 耗散因数 | 相对漏电起痕指数 | ASTMD3638 | 600 | V |
| 绝缘强度 |
| ASTMD149 | 20 | KV/mm |
| 体积电阻率 |
| ASTM D257/IEC 60093 | 10-10 | Ω.cm |
|
|
|
|
|
| 洛氏硬度 |
| ASTMD785 | 80 | M（Scale） |
| ASTMD785 | 120 | R |
|
|
|
|
|
| 防火等级 |
| UL-94 | 0.40mm | V-2 |
| UL-94 | 0.71mm | V-2 |
| UL-94 | 1.50mm | V-2 |
| UL-94 | 3.00mm | V-2 |
| 氧指数 | ASTM2863 | 26 | % |
|
|
|
|
|
| 密度 |
| ASTM D792/ISO 1183 | 1.14 |
|
| 吸水率 23℃/24H |
| ASTM D570/ISO 62 | 2.5 | % |
|
|
|
|
|
| 吸湿率 | 湿 |
| 2.5 | % |
|
|
|
|
|
| 氧指数 | 干 | ASTM D-2863 | 26 | % |
核心提示：代理PA66日本旭化成 ,1402G 玻璃纤维,加纤30%增强,抗热老化性 ,汽车领域